How to Hone an Atypical Aluminum Alloy
Hypereutectic aluminum used for engine blocks contains silicon particles that must be exposed during cylinder honing. This can be done using a cushioning, elastomer honing tool that allows individual abrasive particles to 鈥渂ounce鈥 over the silicon particles.聽
Share
A different type of aluminum alloy is becoming a popular material for engine blocks, one that doesn’t require iron cylinder liners to provide sufficient wear resistance against sliding piston rings. That said, it’s not a new alloy for such applications.
Hypereutectic aluminum is saturated with silicon particles. When a cylinder bore is properly finished, it presents a surface to sliding piston rings that is roughly equivalent to glass. The piston rings contact the slick silicon particles, not the aluminum. This allows hypereutectic-aluminum engines to have reduced friction and weight as well as improved sealing, dimensional stability and heat dissipation versus aluminum blocks with liners.
Porsche used this material for liner-less engine blocks in the 1960s; General Motors briefly used it in the 1970s. Perhaps the biggest manufacturing hurdle those days was the chemical etching process that was required to expose the silicon particles above the bore surface after machining, says Tim Meara, senior honing technician for Sunnen Products Company (Saint Louis, Missouri). In addition to being an intermediate process, chemical etching was subject to intensifying environmental regulations.
Mr. Meara says Sunnen has developed an effective two-stage honing process to replace the etching exposure step. The first step hones a cylinder’s wall to a mirror-like finish using conventional or diamond abrasives. The second step relieves the soft aluminum around the silicon particles to expose the silicon particles.
The silicon-particle exposure step uses an elastomer-bond abrasive and light honing force, Mr. Meara explains. The elastomer-based design overcomes three limitations of a rigid abrasive in the silicon exposure process. First, the cushioning elastomer deforms to allow individual abrasive particles to "bounce" over the silicon particles, yet it also provides the rigidity to cut the aluminum surrounding the particles. Second, the elastomer damps the overall force applied to the abrasive, making the process forgiving of pressure variations from the honing machine’s feed system. (In other words, the honing tool’s diametrical expansion does not have to exactly match the rate at which the cylinder is increasing in diameter from stock removal.) Third, the elastomer conforms to cylinder taper and out-of-roundness, allowing the process to remove very small amounts of material (0.5 micron per side) uniformly throughout the cylinder. With a rigid abrasive, cylinder out-of-roundness would cause variations in abrasive cutting pressure as the honing tool rotates.
The ideal surface should have flats on the silicon particles, particle protrusion ranging from 0.5 to 1 micron above the cylinder surface, and a minimum amount of fractured or torn particles. This exposure step is based on time and typically takes 1 to 1.5 minutes to achieve the 0.5-micron exposure height. Longer cycle times are not harmful because the process is somewhat self-limiting, Mr. Meara says.
Related Content
-
4 Tips for Staying Profitable in the Face of Change
After more than 40 years in business, this shop has learned how to adapt to stay profitable.
-
Eliminating Automotive Defects Per Million With Automated Visual Inspection
This automotive manufacturer virtually eliminated PPM defect complaints after implementing an automated visual inspection system at its facility.
-
DN Solutions Responds to Labor Shortages, Reshoring, the Automotive Industry and More
At its first in-person DIMF since 2019, DN Solutions showcased a range of new technologies, from automation to machine tools to software. President WJ Kim explains how these products are responses to changes within the company and the manufacturing industry as a whole.